产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 55 | g/10min |
| 比重 | ASTM D-792 | 1.17 | 23/23℃ | ||
| 熔体流动速率 | 200℃ 5kg | ASTM D-1238 | 4.8 | g/10min | |
| 机械性能 | IZOD冲击强度 | 1/4〃 | ASTM D-256 | 17 | kg.cm/cm |
| 弯曲强度 | ASTM D-790 | 640 | kg/cm2 | ||
| 弯曲强度 | ASTM D-790 | 9070 | lb/in2 | ||
| 引张强度 | ASTM D-638 | 400 | kg/cm2 | ||
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 3.1 | ft.lb/in | |
| 引张强度 | ASTM D-638 | 5670 | lb/in2 | ||
| IZOD冲击强度 | 1/8" | ASTM D-256 | 21 | kg.cm/cm | |
| 伸长率 | ASTM D-638 | 15 | % | ||
| 洛氏硬度 | ASTM D-785 | 100 | R | ||
| IZOD冲击强度 | 1/8" | ASTM D-256 | 3.8 | ft.lb/in | |
| 弯曲弹性率 | ASTM D-790 | 3.2×105 | lb/in2 | ||
| 弯曲弹性率 | ASTM D-790 | 2.3×104 | kg/cm2 | ||
| 热性能 | 热变形温度 | ASTM D-648 | 85(185) | ℃ | |
| 热变形温度 | ASTM D-648 | 76(169) | ℉ | ||
| 维卡软化点 | ASTM D-1525 | 197 | ℉ | ||
| 燃烧性 | File No. E56070 UL&C-UL | 1/12"V-O，1/10"5VA | |||
| 维卡软化点 | ASTM D-1525 | 92 | ℃ | ||
目录
1 特性
2 注塑工艺
3 应用范围
4 现状
5 五大性能
特性
编辑
ABS塑料是由丙烯腈、丁二烯和苯乙烯三种化学单体合成。每种单体都具有不同特性：丙烯腈有高强度、热稳定性及化学稳定性；丁二烯具有坚韧性、抗冲击特性；苯乙烯具有易加工、高光洁度及高强度。从形态上看，ABS是非结晶性材料。三中单体的聚合产生了具有两相的三元共聚物，一个是苯乙烯-丙烯腈的连续相，另一个是聚丁二烯橡胶分散相。ABS塑胶原料的特性主要取决于三种单体的比率以及两相中的分子结构。
1、综合性能较好、冲击强度较高、化学稳定性、电性能良好。
ABS塑胶制品
2、与有机玻璃的熔接性良好、制成双色塑件、且可表面镀铬、喷漆处理。
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点、比PMMA、PC塑胶原料等好、柔韧性好。5、ABS塑料具有优良的综合性能，有极好的冲击强度、尺寸稳定性好、电性能、耐磨性、抗化学药品性、染色性，成型加工和机械加工较好。6、ABS树脂耐水、无机盐、碱和酸类，不溶于大部分醇类和烃类溶剂，而容易溶于醛、酮、酯和某些氯代烃中。
ABS塑胶原料缺点：热变形温度较低，可燃，耐候性比较差